• ikhanda_isibhengezo_01

I-PVC Resin HS-1300 K70-72 Ibanga Lekhebula

Incazelo emfushane:


  • Intengo ye-FOB:1200-1500 USD/MT
  • Imbobo:Xingang, Qingdao, Shanghai, Ningbo
  • I-MOQ:17MT
  • Inombolo ye-CAS:9002-86-2
  • Ikhodi ye-HS:390410
  • Inkokhelo:TT, LC
  • Imininingwane Yomkhiqizo

    Amapharamitha womkhiqizo

    Umkhiqizo: I-Polyvinyl Chloride Resin
    I-Chemical Formula: (C2H3Cl)n

    Inombolo yeCas: 9002-86-2
    Idethi yokuphrinta: Meyi 10, 2020

    Incazelo

    Ifaka i-thermo plasticity, engancibiliki emanzini, kuphethiloli notshwala, evuvukele noma encibilike ibe yi-ether, i-ketone, i-chlorinated aliphatic hydrocarbons, ne-aromatic hydrocarbon, ukumelana okuphezulu nokugqwala, kanye nempahla enhle ye-dielectric.

    Izinhlelo zokusebenza

    Isetshenziswa kakhulu kumapayipi we-pvc, amaphrofayili ewindi, amafilimu, amashidi, amashubhu, izicathulo, okokufakwayo, njll.

    Ukupakisha

    Esikhwameni se-kraft esingu-25kg noma esikhwameni se-jumbo esingu-1100kg.

    IZINTO

    HS-1300

    HS-1000R

    HS-800

    HS-700

    I-Viscosity(ml/g)

    127-135

    107-118

    87-95

    73-86

    K inani

    71-72

    66-68

    60-62

    55-59

    Inombolo yezinhlayiyana zokungcola ≤

    16

    16

    16

    16

    Ama-Volatiles(incl.water ) %≤

    0.30

    0.30

    0.30

    0.30

    Ukuminyana kwenqwaba g/ml ≥

    0.48

    0.53

    0.53

    0.53

    Isihlungi isilinganiso%

    0.25mm ≤

    1.0

    1.0

    2.0 2.0
    0.063mm ≥

    98

    98

    97 97

    "Iso lezinhlanzi" inombolo yeyunithi /400cm2 ≤

    10

    10

    20 20

    100g resin plasticizer absorbtion g ≥

    28

    19

    16 14

    Ubumhlophe(ngemuva kwe-160℃10min)≥

    80

    80

    80 80

    I-VCM eyinsalela ppm ≤

    1.0 1.0 1.0 1.0

    Ezinye Iziphakamiso Zefomula

    PVC wire box

    I-PVC 100kg,
    I-calcium ekhanyayo 30kg,
    I-Composite Lead Salt Stabilizer 3.6kg,
    I-ACR 2.0kg,
    DOP 3kg,
    I-Stearic Acid 1.0kg,
    Upharafini 0.3kg,
    I-PE Wax 0.35kg,
    I-Brightener 0.02kg,
    I-Titanium Dioxide 1.6kg.

    Ipayipi lepulasitiki lePVC lezokwelapha

    I-PVC 50kg,
    I-Tetraoctyl Pyromellitic Acid 35.52kg,
    Amafutha e-Epoxy Soybean 1.89kg,
    I-Stearic Acid 0.15kg,
    I-CA / Za I-Environmental Stabilizer 1.0kg,
    I-Glycerol 0.048kg,
    I-PE Wax 0.1kg.

    Ipayipi esobala le-PVC

    I-Formula1(Hose):

    I-PVC 100kg,
    I-DOTP 45kg,
    Amafutha e-Epoxy Soybean 5kg,
    I-Stearic Acid 0.4kg,
    I-PE Wax 0.35kg,
    I-Organic Tin 1.5kg.

    I-Formula2(Ipayipi eliqinile):

    I-PVC 100kg,
    I-Organotin 1.4kg,
    I-MBS 5.0kg,
    I-ACR (40) 0.6kg,
    Ukugcotshwa Kwangaphakathi 60 0.6kg, 74 / 70s 0.5kg.

    Ishidi esobala le-PVC

    I-PVC (SG-7 / 8) 100kg,
    I-Organotin 0.8-1.2kg,
    I-ACR (40) 0.8kg,
    I-MBS 2-4, ok-60 0.8, 70s 0.5kg,
    I-Fluorescent Brightener 0.002kg,
    I-Ultramarine 0.001kg.

    Isakhiwo se-PVC formwork

    Ifomula1:

    I-PVC (SG-8) 50kg,
    I-calcium ekhanyayo 25kg,
    I-Composite Lead Salt Stabilizer 2.3kg,
    I-White Foaming Agent 0.45kg,
    I-ejenti Yogwebu AC 0.3kg,
    Ufulawa wezinkuni 10kg,
    PVC Recycled Material 20kg,
    Isilawuli Sokuphuma Amagwebu (80) 4kg,
    CPE 2kg,
    I-Stearic Acid 0.35kg,
    I-PE Wax 0.25kg.

    Ifomula2:

    I-PVC 75kg,
    I-Calcium Elula 35kg,
    Recycling 50kg,
    I-Foaming Board Waste 20kg,
    I-Lead Salt Composite Stabilizer 3.6kg,
    I-Foaming Regulator (533) 9.5kg,
    I-PE Wax 0.55kg,
    Oa6 noma 316a 0.5kg,
    I-AC Foaming Agent 0.3kg,
    I-White Foaming Agent NC 0.8kg.