| Cha. | Izakhiwo ze-Resin | Inani elijwayelekile | Iyunithi | Indlela Yokuhlola |
| 1 | I-Specific Gravity, 23℃ | 1.05 | g/cm³ | I-ASTM D792 |
| 2 | Isikhunta Shrinkage, 23℃, 3.2mm, 23℃ | 0.4-0.7 | % | I-ASTM D955 |
| 3 | Melt Flow Rate, 220 ℃, 10kg | 22 | g/10 min | I-ASTM D1238 |
| 4 | Amandla Okuqina Ekukhiqizweni, 23℃, 50mm/min, 3.2mm | 49 | I-MPa | I-ASTM D638 |
| 5 | I-Tensile Elongation at Yield, 23℃, 50mm/min, 3.2mm | 5 | %, (Amaminithi) | I-ASTM D638 |
| 6 | I-Tensile Elongation at Break, 23'℃, 50mm/min, 3.2mm | 10 | %, (Amaminithi) | I-ASTM D638 |
| 7 | I-Tensile Modulus, 23℃, 50mm/min, 3.2mm | 2350 | I-MPa | I-ASTM D638 |
| 8 | Amandla e-Flexural, 23℃, 15mm/min, 3.2mm | 78 | I-MPa | I-ASTM D790 |
| 9 | I-Flexural Modulus, 23℃, 15mm/min, 3.2mm | 2550 | I-MPa | I-ASTM D790 |
| 10 | I-Izod Impact Amandla, Notched, 3.2mm, 23℃ | 220 | J/m | I-ASTM D256 |
| 11 | I-Izod Impact Amandla, Notched, 3.2mm, -30℃ | 90 | J/m | I-ASTM D256 |
| 12 | I-Izod Impact Amandla, Notched, 6.4mm, 23℃ | 220 | J/m | I-ASTM D256 |
| 13 | I-Izod Impact Amandla, Notched, 6.4mm,-30℃ | 90 | J/m | I-ASTM D256 |
| 14 | I-Rockwell Hardness, i-R-Scale | 110 | / | I-ASTM D785 |
| 15 | I-HDT, i-Edgewise, i-1.82MPa, i-6.4mm, engafakiwe | 85 | °C | I-ASTM D648 |
| 16 | VICAT, 50N, 50℃/h | 92 | °C | I-ASTM D1525 |
| 17 | I-RTI Electrical | 95 | °C | I-UL 746B |
| 18 | I-RTI Mechanical ene-Impact | 95 | °C | I-UL 746B |
| 19 | I-RTI Mechanical ngaphandle kwe-Impact | 95 | °C | I-UL 746B |
| 20 | Ukuvutha, 1.5mm | HB | / | I-UL94 |
| 21 | Ukuvutha, 3.0mm | HB | / | I-UL94 |